Composites of high-temperature thermomechanical pulps and polylactic acid

Research output: Contribution to journalArticleScientificpeer-review

Standard

Composites of high-temperature thermomechanical pulps and polylactic acid. / Solala, Iina; Koistinen, Antti; Siljander, Sanna; Vuorinen, Jyrki; Vuorinen, Tapani.

In: BioResources, Vol. 11, No. 1, 2016, p. 1125-1140.

Research output: Contribution to journalArticleScientificpeer-review

Harvard

APA

Vancouver

Author

Solala, Iina ; Koistinen, Antti ; Siljander, Sanna ; Vuorinen, Jyrki ; Vuorinen, Tapani. / Composites of high-temperature thermomechanical pulps and polylactic acid. In: BioResources. 2016 ; Vol. 11, No. 1. pp. 1125-1140.

Bibtex - Download

@article{63de33d1501244b49804750fb2790c11,
title = "Composites of high-temperature thermomechanical pulps and polylactic acid",
abstract = "High-temperature thermomechanical pulps (HT-TMP, defibrated at 150 to 170 °C) were compared to a reference TMP (defibrated at 130 °C) as a reinforcement for polylactic acid (PLA). Composites were prepared by melt compounding, followed by injection molding, gradually increasing the used fiber content from 0 to 20 wt.{\%}. The injection-molded specimens were characterized by tensile and impact strength tests, scanning electron microscopy, water absorption tests, and differential scanning calorimetry. The TMP fiber damage was also characterized before and after melt compounding by optical analysis. At 20{\%} fiber content, the Young's modulus increased significantly, while the tensile strength remained unchanged and the impact strength decreased slightly. All fibers suffered damage during melt compounding, but the tensile strength remained about the same as in pure PLA. All types of TMP were able to increase the PLA rate of crystallization. The HT-TMP fibers were dispersed more evenly in PLA than the 130 °C TMP. The 170 °C TMP produced composites of lower water absorption than the other two TMP types, probably because of its lower hemicellulose content and its higher surface coverage by lignin.",
keywords = "High-temperature thermomechanical pulp, Hydrophobic fibers, Mechanical properties, Polylactic acid, Thermal properties, Wood fiber composites",
author = "Iina Solala and Antti Koistinen and Sanna Siljander and Jyrki Vuorinen and Tapani Vuorinen",
year = "2016",
doi = "10.15376/biores.11.1.1125-1140",
language = "English",
volume = "11",
pages = "1125--1140",
journal = "BioResources",
issn = "1930-2126",
publisher = "NORTH CAROLINA STATE UNIV DEPT WOOD & PAPER SCI",
number = "1",

}

RIS (suitable for import to EndNote) - Download

TY - JOUR

T1 - Composites of high-temperature thermomechanical pulps and polylactic acid

AU - Solala, Iina

AU - Koistinen, Antti

AU - Siljander, Sanna

AU - Vuorinen, Jyrki

AU - Vuorinen, Tapani

PY - 2016

Y1 - 2016

N2 - High-temperature thermomechanical pulps (HT-TMP, defibrated at 150 to 170 °C) were compared to a reference TMP (defibrated at 130 °C) as a reinforcement for polylactic acid (PLA). Composites were prepared by melt compounding, followed by injection molding, gradually increasing the used fiber content from 0 to 20 wt.%. The injection-molded specimens were characterized by tensile and impact strength tests, scanning electron microscopy, water absorption tests, and differential scanning calorimetry. The TMP fiber damage was also characterized before and after melt compounding by optical analysis. At 20% fiber content, the Young's modulus increased significantly, while the tensile strength remained unchanged and the impact strength decreased slightly. All fibers suffered damage during melt compounding, but the tensile strength remained about the same as in pure PLA. All types of TMP were able to increase the PLA rate of crystallization. The HT-TMP fibers were dispersed more evenly in PLA than the 130 °C TMP. The 170 °C TMP produced composites of lower water absorption than the other two TMP types, probably because of its lower hemicellulose content and its higher surface coverage by lignin.

AB - High-temperature thermomechanical pulps (HT-TMP, defibrated at 150 to 170 °C) were compared to a reference TMP (defibrated at 130 °C) as a reinforcement for polylactic acid (PLA). Composites were prepared by melt compounding, followed by injection molding, gradually increasing the used fiber content from 0 to 20 wt.%. The injection-molded specimens were characterized by tensile and impact strength tests, scanning electron microscopy, water absorption tests, and differential scanning calorimetry. The TMP fiber damage was also characterized before and after melt compounding by optical analysis. At 20% fiber content, the Young's modulus increased significantly, while the tensile strength remained unchanged and the impact strength decreased slightly. All fibers suffered damage during melt compounding, but the tensile strength remained about the same as in pure PLA. All types of TMP were able to increase the PLA rate of crystallization. The HT-TMP fibers were dispersed more evenly in PLA than the 130 °C TMP. The 170 °C TMP produced composites of lower water absorption than the other two TMP types, probably because of its lower hemicellulose content and its higher surface coverage by lignin.

KW - High-temperature thermomechanical pulp

KW - Hydrophobic fibers

KW - Mechanical properties

KW - Polylactic acid

KW - Thermal properties

KW - Wood fiber composites

U2 - 10.15376/biores.11.1.1125-1140

DO - 10.15376/biores.11.1.1125-1140

M3 - Article

VL - 11

SP - 1125

EP - 1140

JO - BioResources

JF - BioResources

SN - 1930-2126

IS - 1

ER -