Er3+-Al2O3 nanoparticles doping of borosilicate glass

Research output: Contribution to journalArticleScientificpeer-review

Details

Original languageEnglish
Pages (from-to)1407-1410
Number of pages4
JournalBulletin of Materials Science
Volume38
Issue number5
DOIs
Publication statusPublished - Sep 2015
Publication typeA1 Journal article-refereed

Abstract

Novel borosilicate glasses were developed by adding in the glass batch Er3+-Al2O3 nanoparticles synthetized by using a soft chemical method. A similar nanoparticle doping with modified chemical vapour deposition (MCVD) process was developed to increase the efficiency of the amplifying silica fibre in comparison to using MCVD and solution doping. It was shown that with the melt quench technique, a Er3+-Al2O3 nanoparticle doping neither leads to an increase in the Er3+ luminescence properties nor allows one to control the rare-earth chemical environment in a borosilicate glass. The site of Er3+ in the Er3+-Al2O3 nanoparticle containing glass seems to be similar as in glasses with the same composition prepared using standard raw materials. We suspect the Er3+ ions to diffuse from the nanoparticles into the glass matrix. There was no clear evidence of the presence of Al2O3 nanoparticles in the glasses after melting.

Keywords

  • Glass, optical fibre, IR photoluminescence, nanoparticles, doping, LUMINESCENCE, IONS