Failure analysis of a leaching reactor made of glass-fiber reinforced plastic

Tutkimustuotosvertaisarvioitu

Yksityiskohdat

AlkuperäiskieliEnglanti
Sivut117-136
JulkaisuEngineering Failure Analysis
Vuosikerta60
Varhainen verkossa julkaisun päivämäärä17 marraskuuta 2015
DOI - pysyväislinkit
TilaJulkaistu - 2016
OKM-julkaisutyyppiA1 Alkuperäisartikkeli

Tiivistelmä

This paper reports a failure analysis of a leaching reactor in a zinc plant that suffered from a catastrophic failure after less than two years of operation. During normal operation the bottom of the reactor fell out suddenly, releasing the contents, a high-temperature acidic solution, into the surroundings in an uncontrollable manner. The reactor was made of glass-fiber reinforced plastic. Microscopy, thermal analysis, mechanical testing and finite element analyses were employed to investigate the causes of the failure. There were several contributing factors but the root cause was poor adhesion between the bottom and the joint laminate, which was caused by insufficient grinding during the surface preparation stage of the joint.

!!ASJC Scopus subject areas

Tutkimusalat

Julkaisufoorumi-taso

Tilastokeskuksen tieteenalat