Low temperature afterglow from SrAl2O4: Eu, Dy, B containing glass

Tutkimustuotosvertaisarvioitu

Yksityiskohdat

AlkuperäiskieliEnglanti
Sivut86-90
Sivumäärä5
JulkaisuScripta Materialia
Vuosikerta190
DOI - pysyväislinkit
TilaE-pub ahead of print - 2020
OKM-julkaisutyyppiA1 Alkuperäisartikkeli

Tiivistelmä

SrAl2O4: Eu, Dy, B particles were added in a phosphate glass (90NaPO3-10NaF (in mol%)) using the direct doping method. For the first time, the composition of the particles prior to and after embedding them in the glass was analysed using EPMA analysis. Boron was found to be incorporated in already distorted surroundings creating new trapping centers in the particles which are thought to be favourable for the tunnelling process and so for the afterglow at 10K. Despite the partial decomposition of the particles, the glass exhibit afterglow at low temperature confirming to be promising materials for low temperature applications.