Quenching and Partitioning of Multiphase Aluminum-Added Steels

Tutkimustuotosvertaisarvioitu

Yksityiskohdat

AlkuperäiskieliEnglanti
Artikkeli373
Sivumäärä17
JulkaisuMetals
Vuosikerta9
Numero3
DOI - pysyväislinkit
TilaJulkaistu - 22 maaliskuuta 2019
OKM-julkaisutyyppiA1 Alkuperäisartikkeli

Tiivistelmä

The quenching and partitioning response following intercritical annealing was investigated for three lean TRIP-type High-Al steel compositions. Depending on the intercritical austenite fraction following annealing, the steels assumed either a ferrite/martensite/retained austenite microstructure or a multiphase structure with ferritic, bainitic and martensitic constituents along with retained austenite. The amount of retained austenite was found to correlate with the initial quench temperature and, depending on the intercritical annealing condition prior to initial quenching, with the uniform and ultimate elongations measured in tensile testing.

Tutkimusalat

Julkaisufoorumi-taso

Tilastokeskuksen tieteenalat