Regeneration of fibres from alkaline solution containing enzyme-treated 3-allyloxy-2-hydroxypropyl substituted cellulose

Tutkimustuotosvertaisarvioitu

Yksityiskohdat

AlkuperäiskieliEnglanti
Sivut2271-2282
Sivumäärä12
JulkaisuCellulose
Vuosikerta22
Numero4
DOI - pysyväislinkit
TilaJulkaistu - 10 toukokuuta 2015
OKM-julkaisutyyppiA1 Alkuperäisartikkeli

Tiivistelmä

The aim of this study was to regenerate fibres from the alkaline cellulose solution containing 3-allyloxy-2-hydroxypropyl substituents. Enzyme-treated cellulose was modified in alkaline aqueous tert-butanol (tBuOH) using allyl glycidyl ether (AGE) as the modification reagent. 3-allyloxy-2-hydroxypropyl substituted (AHP) enzyme-treated cellulose with DS<inf>A</inf> 0.05 was obtained. Enzyme-treated cellulose without (reference) and with substituents were dissolved in sodium zincate using the freezing-thawing cycle. The reference solution alone and the mixture solutions containing 10 or 25 % of the AHP cellulose were regenerated into cellulosic fibres using the wet spinning technique. The solutions containing 100 or 50 % of the AHP cellulose did not form fibres in acidic bath. The 10 % share of AHP cellulose did not affect the mechanical properties of the fibres (1.5 cN dtex<sup>−1</sup>), while the 25 % share decreased the tenacity slightly (1.3 cN dtex<sup>−1</sup>). Elongation of the fibres ranged from 18 to 22 %. The 10 and 25 % shares of AHP cellulose increased the water holding ability of fibres by 12 and 33 %, respectively. According to FESEM the fibre structures are composed of nanosized fibrils.

!!ASJC Scopus subject areas

Tutkimusalat

Julkaisufoorumi-taso

Tilastokeskuksen tieteenalat