The role of (FeCrSi)2(MoNb)-type Laves phase on the formation of Mn-rich protective oxide scale on ferritic stainless steel

Tutkimustuotos: vertaisarvioituArtikkeli

Yksityiskohdat

AlkuperäiskieliEnglanti
Sivut214-222
JulkaisuCorrosion Science
Vuosikerta132
DOI - pysyväislinkit
TilaJulkaistu - maaliskuuta 2018
OKM-julkaisutyyppiA1 Alkuperäisartikkeli

Tiivistelmä

Microalloying of stainless steel with reactive elements increases oxidation resistance but makes the alloy prone to microstructural changes. XPS results reveal changes in the initial oxidation mechanism on Ti–Nb stabilized ferritic stainless steel (EN 1.4521) after 120 h heat treatment at 650 °C. Age-precipitation of (FeCrSi)2(MoNb)-type Laves phase resulted in less pronounced surface segregation and oxidation of microalloying elements. Si oxidizes preferentially at the Laves precipitate locations via outward diffusion forming diffusion barrier for the other scale forming elements. Most significantly the diffusion of Mn and the formation of low volatile (Mn,Cr)3O4 spinel oxide at the surface was strongly suppressed.

Julkaisufoorumi-taso

Tilastokeskuksen tieteenalat

TTY:n teema-alueet