The role of microstructure in high stress abrasion of white cast irons

Tutkimustuotos

Yksityiskohdat

AlkuperäiskieliEnglanti
OtsikkoThe 17th Nordic Symposium on Tribology - NORDTRIB 2016 14th - 17th June 2016 Aulanko, Hämeenlinna, Finland
TilaJulkaistu - 2016
OKM-julkaisutyyppiD3 Artikkeli ammatillisessa konferenssijulkaisussa
TapahtumaNORDIC SYMPOSIUM ON TRIBOLOGYNORDTRIB: NORDTRIB -
Kesto: 1 tammikuuta 1900 → …

Conference

ConferenceNORDIC SYMPOSIUM ON TRIBOLOGYNORDTRIB
Ajanjakso1/01/00 → …

Tiivistelmä

The abrasion wear resistance of white cast irons can be controlled primarily by adjusting the size, size distribution, and volume fraction of the carbide phase. The main physical property of white cast irons correlating with abrasion resistance is hardness. This study concentrates on the evaluation of hardened and stress relieved, normalized, self-hardened, and as-cast states of high chromium white cast irons in high stress abrasion. The correct size and orientation of the carbides were found to be crucial for the wear resistance of white cast irons in high stress abrasive conditions. The different annealing procedures affected the formation of the carbide structure and its distribution, as well as the microstructure of the matrix. The austenite-to-martensite ratio together with a beneficial carbide structure was found to have a strong effect on the abrasion wear resistance of WCI specimens.