Upconversion from fluorophosphate glasses prepared with NaYF4:Er3+,Yb3+nanocrystals

Tutkimustuotosvertaisarvioitu

Yksityiskohdat

AlkuperäiskieliEnglanti
Sivut19226-19236
Sivumäärä11
JulkaisuRSC Advances
Vuosikerta8
Numero34
DOI - pysyväislinkit
TilaJulkaistu - 1 tammikuuta 2018
OKM-julkaisutyyppiA1 Alkuperäisartikkeli

Tiivistelmä

The direct doping method was applied to fabricate upconverter fluorophosphate glasses in the system (90NaPO3-(10-x)Na2O-xNaF) (mol%) by adding NaYF4:Er3+,Yb3+ nanocrystals. An increase in the network connectivity, a red shift of the optical band gap and a decrease in the thermal properties occur when Na2O is progressively replaced by NaF. To ensure the survival and the dispersion of the nanocrystals in the glasses with x = 0 and 10, three doping temperatures (Tdoping) (525, 550 and 575 °C) at which the nanocrystals were added in the glass melt after melting and 2 dwell times (3 and 5 minutes) before quenching the glasses were tested. Using 5 wt% of the NaYF4:Er3+,Yb3+ nanocrystals, green emission from the NaYF4:Er3+,Yb3+ nanocrystals-containing glasses was observed using a 980 nm pumping, the intensity of which depends on the glass composition and on the direct doping parameters (Tdoping and dwell time). The strongest upconversion was obtained from the glass with x = 10 prepared using a Tdoping of 550 °C and a 3 min dwell time. Finally, we showed that the upconversion, the emission at 1.5 μm and of the transmittance spectra of the nanocrystals-containing glasses could be measured to verify if decomposition of the nanocrystals occurred in glass melts during the preparation of the glasses.

!!ASJC Scopus subject areas

Julkaisufoorumi-taso

Tilastokeskuksen tieteenalat

Latausten tilastot

Ei tietoja saatavilla